EPDM waterproof membrane is made from ethylene propylene diene monomer (EPDM), adding into some chemical auxiliaries,
for example, carbon black, nanophase modifier, plasticizer, vulcanization accelerator and others,
it is one kind of polymer waterproof membrane with excellent performance elasticity.
| EPDM waterproofing membrane | |
| Material | EPDM rubber |
| Thickness | from 0.7mm to 2.0mm |
| Width | 1m, 2m, 3m, 4m...8m at mos |
| Length | 20m/roll |
| Color | Black |
| Packaging | Non woven bag |
| Type | homogeneous , backing with fabric , self adhesive |
| Application | roofing,ponds,pools,fish farm,others |
|
No. |
Items |
JL1 |
JL2 |
|
|
1 |
Tensile Strength (MPa) |
23ºC |
≥7.5 |
≥4.0 |
|
|
|
60ºC |
≥2.3 |
≥0.8 |
|
2 |
Breaking Elongation |
23ºC |
≥450% |
≥400% |
|
|
|
-20ºC |
≥200% |
≥200% |
|
3 |
Tear Strength kN/m |
≥25 |
≥18 |
|
|
4 |
Impermeability, 0.3Mpa, 30 minutes |
No leaking |
No leaking |
|
|
5 |
Low Temperature Flexibility |
-40ºC |
-30ºC |
|
|
6 |
Thermal Stability (mm) |
Extend |
≤2 |
≤2 |
|
|
|
Shrink |
≤4 |
≤4 |
|
7 |
Hot Air Aging (80ºC×168h) |
Tensile Retention |
≥80% |
≥90% |
|
|
|
Breaking Elongation Retention |
≥70% |
≥70% |
|
8 |
Alkali Resistance, saturated Ca(OH)2 solution, 23ºC×168h |
Tensile Retention |
≥80% |
≥80% |
|
|
|
Breaking Elongation Retention |
≥80% |
≥90% |
|
9 |
Ozone Aging(40ºC×168h) |
Elongation 40%, 500pphm |
No crack |
No crack |
|
10 |
Artificial Weathering Aging |
Tensile Retention |
≥80% |
≥80% |
|
|
|
Breaking Elongation Retention |
≥70% |
≥70% |
|
11 |
Bonding Peel Strength (Sheet and Sheet) |
N/mm (Standard test conditions) |
≥1.5 |
≥1.5 |
|
|
|
Soaking retention rate(23ºC×168h) |
≥70% |
≥70% |